Copolymer 4084 is a nonionic emulsifier for emulsion polymerization. This pale-yellow wax is composed of block copolymer of propylene oxide and ethylene oxide. Copolymer 4084 is used in emulsion polymerization of monomers like pure acrylic, styrene-acrylic acid esters and vinyl acetate, polyvinyl acetate, acrylate and styrene/acrylate dispersions to stabilize the rheological behavior of the polymer dispersions and to improve the electrolyte and shear stability. It can be used in combination with other nonionic, anionic and cationic surfactants. It is compatible with vinyl and acrylic resins. It reduces the amount of coagulum formed during the polymerization and improves the final latex property.
TEST |
Standard Test Method |
result |
Appearance at 20°C |
— |
Pale yellow wax |
Active content |
— |
100% |
Melting point |
ASTM D-1209 |
48 °C |
pH (5% in water) |
ASTM D-1172 |
6-8 |
Cloud point, °C (1g in 100 ml 10% NaCl solution) |
ASTM D-2024 |
69±3 |
Density at 80°C, g/ml |
ASTM D-1298 |
1.04±0.02 |
HLB, calculated |
Calculated |
13 |
Viscosity at 80°C, cP |
ASTM D-445 |
2300 |
Copolymer 4084 is dispatched in polyethylene or corrugated steel, galvanized or carbon steel drums. Copolymer 4084 is stable for 2 years when stored in the original sealed containers in a cool and dry place.
Precautions for safe handling
Avoid contact with skin and eyes. Avoid formation of dust and aerosols.
Provide appropriate exhaust ventilation at places where dust is formed. Normal measures for preventive fire protection.
Conditions for safe storage
Keep container tightly closed in a dry and well-ventilated place.
Inhalation : May be harmful if inhaled. May cause respiratory tract irritation.
Skin : May be harmful if absorbed through skin. May cause skin irritation.
Eyes : May cause eye irritation.
Ingestion : May be harmful if swallowed.
Copolymer 4084 is a nonionic emulsifier recommended for:
- Copolymer 4084 is a nonionic emulsifier for emulsion polymerization.
- It is used in emulsion polymerization of polyvinyl acetate, acrylate and styrene/acrylate dispersions to stabilize the rheological behavior of the polymer dispersions and to improve the electrolyte and shear stability.
- Styrene/acrylate dispersions.
- Acrylate dispersions.
- Vinyl acetate dispersions.